4 Welding Hints
Because of the multitude of and great differences in the important points for welding only the very basic
operations for the most common electrodes for low-carbon steels, the Ti-type electrode, are introduced here.
In the case that other electrodes have to be used, the electrode manufacturers supply upon request all relevant
information for the type of special electrode to be used.
Always make some trial welds on scrap material. Select electrode diameter and welding current as per Table 1.
Attach earth clamp to work piece and place electrode into electrode holder as described earlier. Now hold the
electrode tip approx. 2 cm / 1 inch above the starting point of your welding seam. Hold the welding shield in front
of your face and draw the electrode with a short stroke along the groove. Through the welding shield you watch
the arc, keeping it to a length of 1 to 1.5 times the electrode diameter.
wrong
arc too long
(Pic. 3)
correct
approx. 1 - 1.5 the electrode-Ø
(Pic. 4)
The correct arc length is important for a good weld, because with too short or too long an arc both welding current
and working voltage change. A low working voltage causes insufficient penetration. Too high or too low welding
current gives a poor welding seam. Too long an arc does not sufficiently melt the parent material, resulting in
high spatter losses. Also the air, with its detrimental substances like hydrogen and nitrogen, may get access to
the weld pool.
For a good weld the work angle of the electrode (or electrode inclination angle) is of substantial importance. The
inclination should be 70° - 80° to the welding direction. With the work angle too steep slag will run under the weld
pool, too flat an work angle causes the arc to spatter, in both cases the result is a porous, weak welding seam
(see pictures 5 - 7).
< 70°
welding direction
(Pic. 6)
(Pic. 5)
> 80°
welding direction
(Pic. 7)
70-80°
welding direction
wrong
wrong correct
The welder has to keep the arc at the same length, that is the electrode burn-off is compensated by feeding the
electrode into the weld. At the same time the welder has to watch the weld pool for even penetration and width.
Welding is always done from left to right (backhand welding).
At the end of the welding seam the electrode can not simply be lifted or pulled from the weld, this creates porous
end craters, which weaken the weld. To correctly terminate a weld the electrode is held for a short moment at
the end of the weld seam, then lifted in an arc over the just laid weld.
wrong
(Pic. 8)
correct
(Pic. 9)
Remove slag only after it has cooled down and is no longer glowing.
If an interrupted weld is to be continued, the slag at the end of the already finished weld must be removed. Then
the arc can be started either in the groove or on the weld, as described earlier, and then moved to the end of
the weld, which has to be thoroughly melted for good fusion. Welding is then continued normally.
19
… 9 …


Need help? Post your question in this forum.

Forumrules


Report abuse

Libble takes abuse of its services very seriously. We're committed to dealing with such abuse according to the laws in your country of residence. When you submit a report, we'll investigate it and take the appropriate action. We'll get back to you only if we require additional details or have more information to share.

Product:

For example, Anti-Semitic content, racist content, or material that could result in a violent physical act.

For example, a credit card number, a personal identification number, or an unlisted home address. Note that email addresses and full names are not considered private information.

Forumrules

To achieve meaningful questions, we apply the following rules:

Register

Register getting emails for Elektra Beckum MIG 140 at:


You will receive an email to register for one or both of the options.


Get your user manual by e-mail

Enter your email address to receive the manual of Elektra Beckum MIG 140 in the language / languages: English as an attachment in your email.

The manual is 0,38 mb in size.

 

You will receive the manual in your email within minutes. If you have not received an email, then probably have entered the wrong email address or your mailbox is too full. In addition, it may be that your ISP may have a maximum size for emails to receive.

The manual is sent by email. Check your email

If you have not received an email with the manual within fifteen minutes, it may be that you have a entered a wrong email address or that your ISP has set a maximum size to receive email that is smaller than the size of the manual.

The email address you have provided is not correct.

Please check the email address and correct it.

Your question is posted on this page

Would you like to receive an email when new answers and questions are posted? Please enter your email address.



Info